E-COATING - Metal ThermalShield

ReHarmony E-COATING - Metal ThermalShield is an eco-friendly anti-rust coating that uses water as the dispersion medium. Formulated with multiple physical and chemical rust prevention mechanisms, it delivers a matte decorative finish.

With excellent environmental performance, strong rust protection, and quick drying properties, it ensures convenient application, strong adhesion, and good weather resistance, making it an ideal solution for long-lasting surface protection.

• Color: White (custom tintable)

• Composition: Water-based resin, pigments/fillers, additives, water

• Application Methods: Brush, roller, or spray

• Coverage: 4–5 m²/L (two coats)

• Dilution: 5–10% water addition

• Dry Film Thickness: 30–80 μm

• Drying Time (25°C, 50% RH): 24–48 hours

• Recoat Time (25°C, 50% RH): 12–24 hours

• Solid Content: 40–60%

• Shelf Life: 12–18 months

• Recommended Coating System:

  • Primers: Water-based epoxy primer, water-based zinc-rich primer

  • Intermediate Coat: Water-based epoxy micaceous iron oxide

  • Topcoats: Water-based acrylic, water-based polyurethane

  • Thinner: Compatible water-based thinner

    Note: Actual consumption and coverage may vary depending on application method, surface porosity/roughness, and environmental conditions. For optimal results, ensure proper surface preparation and follow manufacturer's instructions.

Product Specifications

Great Cooling Performance

Exceptional Stain Resistance

Feature

Superior Weather and Biological Resistance

Environmentally Friendly and Health-Conscious

Surface Preparation Technical Requirements

Oil and Grease Removal

• To remove oil, grease, and dirt from metal surfaces, use organic solvents such as white spirit or trichloroethylene for wiping, or employ alkaline degreasers for cleaning.

• Ultrasonic cleaning equipment can also be used to aid in oil removal, ensuring the surface is free of oil residues.

Rust Removal

• For surfaces with light rust, manual or power tools like wire brushes and sandpaper can be used to grind away rust.

• For heavily corroded surfaces, sandblasting is recommended to thoroughly remove rust layers, oxide scales, and other impurities, achieving a certain level of surface roughness to enhance paint adhesion. After sandblasting, the surface should meet the Sa2.5 grade or higher, meaning it should be free of visible grease, dirt, oxide scales, rust, and old paint coatings, with any remaining marks being only slight specks or streaks.

Surface Cleaning

• Use clean compressed air or a vacuum cleaner to remove dust and debris from the surface after rust removal. Alternatively, wipe with a clean soft cloth or solvent to ensure the surface is free of dust and debris, providing a clean base for subsequent painting.

Surface Roughness Treatment

• Surface roughness is typically controlled through sandblasting or shot blasting. The appropriate roughness range is usually between 30-75μm, which can be measured using a roughness gauge.

Drying Treatment

• The treated surface should be thoroughly dried, with surface moisture content generally required to be below 8%. Moisture on the surface can affect paint adhesion, leading to issues such as blistering and peeling of the coating.

• Drying methods include natural air drying, hot air blowing, or infrared lamp drying, with drying time varying based on environmental temperature and humidity as well as the surface treatment method. If chemical treatment is used, rinse with clean water and dry to prevent moisture retention that could cause blistering and peeling of the paint layer.

Avoiding Secondary Contamination

• The treated surface should be protected from re-exposure to oil, dust, and other contaminants. If temporary storage is necessary, protective measures such as covering with plastic film should be taken.